Grade 310S stainless steel is superior than 304 or 309 stainless steel in most environments, because it has high nickel and chromium content. It has high corrosion resistance and strength in temperatures up to 1149°C (2100°F). The lower carbon content of 310S does reduce its high temperature strength compared to 310.
Grade 310S stainless steel is superior than 304 or 309 stainless steel in most environments, because it has high nickel and chromium content. It has high corrosion resistance and strength in temperatures up to 1149°C (2100°F). The lower carbon content of 310S does reduce its high temperature strength compared to 310.
Product Description
| Grade | ASTM S31008,310S / GBS31008,06Cr25Ni20 /JIS SUS310S |
| Available Standard | ASTM, AISI, SUS, JIS, EN, DIN, GB, ASME, etc. In general, ASTM A240/A240M or as your requirements |
| Certification | MTC from mill |
| Brand/MILL | JISCO,PZSS,BAO Steel,etc |
| Treatment | Cold Rolled |
| Thickness | 0.3mm-3mm,4mm-6mm |
| Width | ≤2000mm |
| Finish | 2B |
| Edge | Slit edge & Mill edge |
Specification
310S stainless steel Chemical Composition
| rade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 310S | min. | - | - | - | - | - | 24 | - | 19 | - |
| max. | 0.08 | 2 | 1.5 | 0.045 | 0.03 | 26 | 22 |
Mechanical Properties
Mechanical properties of 310S grade stainless steel
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50 mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 310S | 515 | 205 | 40 | 95 | 217 |
Physical Properties
Physical properties of 310S grade stainless steel in the annealed condition
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (μm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100°C (J/kg.K) | Electrical Resistivity (nΩ.m) | |||
| 0-100 °C | 0-315 °C | 0-538 °C | at 100 °C | at 500 °C | |||||
| 310S | 7750 | 200 | 15.9 | 16.2 | 17 | 14.2 | 18.7 | 500 | 720 |
310 Stainless Steel Grade Specification Comparison
| Grade | CN GB/T20878-2007 | USA ASTMA959-2004 | EUROPE EN10088:1-1995, EN10095-1999 | JIS G4303-1998 JIS G4311-1991 | |||
| S31008 | 06Cr25Ni20 | S31008 | 310S | X12CrNi23-12 | 1.4845 | SUS310S | |
Applications
Boiler baffles
Furnace components
Oven linings
Fire box sheets
Other high temperature containers.
In 2016, it signed a strategic cooperation agreement with major domestic stainless steel factories for the sales of medium and heavy plates and special steel products, which also enabled the company to have new and brighter sales varieties. At the same time, it provides one-stop service for cutting, cutting, forming and and surface processing of stainless steel.